In this work, the addition of a combination of Graphene Oxide Nanoplatelets (GONPs) and Ground
Granulated Blast Furnace Slag (GGBFS) was studied as admixture in concrete. Tests on physical and mechanical
properties and chloride permeability were conducted. GGBFS was replaced with Ordinary Portland Cement (OPC)
and it was determined that GGBFS Up to 50% by weight improves the physical and mechanical properties of
concrete. GONPs with an optimal amount of 50% by weight of GGBFS were added to the concrete and the physical
and mechanical properties of the samples were determined. It was observed that the addition of GONPs was effective
in improving the mechanical strength and physical properties of specimens. The results indicated that addition of
0.1 wt.% GO and 50 wt.% GGBFS would increase the compressive strength of the concrete sample up to 42.7%
during 28 days and 46% during 90 days compared to OPC. Concrete with a combination of 0.1 wt.% GONPs and
50 wt.% GGBFS witnessed an increase in its flexural strength up to 58.5% during 28 days and 59.2% during 90
days. The results indicated that by adding 0.1 wt.% GO and 50 wt.%, concrete chloride permeability decreased
substantially 72% for 90 day cured samples compared to OPC. GONPs as an alternative to cement up to 0.1% by
weight can accelerate the formation of C-S-H gel, thereby increasing the strength and improving the resistance of
water absorption and chloride permeability. The effects of pozolanic reaction in the concrete leading to the filling
of the pores were significant factors in the proposed curtailment mechanism

Keywords: Concrete, Durability, Graphene Oxide, Ground Granulated Blast Furnace Slag