Comparative Analysis on Reinforcement of Potential Additives in WOKA
Cermet HVOF Coating Subjected to Slurry Erosion in Ash Conditions

Singh, Jashanpreet; Gill, Rana; Kumar, Satish; Mohapatra, S.K.

doi:10.22068/ijmse.2834

Volume 19, Issue 4 (Desember 2022) IJMSE 2022, 19(4): 1-12 | Back to browse issues page

‎ 10.22068/ijmse.2834

Mendeley

Zotero

RefWorks

Singh J, Gill R, Kumar S, Mohapatra S. Comparative Analysis on Reinforcement of Potential Additives in WOKA Cermet HVOF Coating Subjected to Slurry Erosion in Ash Conditions. IJMSE 2022; 19 (4) :1-12
URL: http://ijmse.iust.ac.ir/article-1-2834-en.html

Comparative Analysis on Reinforcement of Potential Additives in WOKA Cermet HVOF Coating Subjected to Slurry Erosion in Ash Conditions

Jashanpreet Singh

, Rana Gill

, Satish Kumar

, S.K. Mohapatra

Abstract: (7117 Views)

In this paper, an investigation was carried out to test the suitability of potential additive materials in
WOKA 3533 (WC-10Co4Cr) cermet HVOF coating subjected to slurry erosion in ash conditions. The additives
namely molybdenum carbide, yttrium oxide, and zirconium oxide were added in equal percentages (3 wt.%) in
WOKA cermet powder. High-velocity oxy-fuel (HVOF) spraying was performed to develop the additive-based
WOKA cermet coatings. The slurry erosion in ash conditions was tested using the pot tester. Microstructural and
mechanical properties of traditional and additive-based WOKA cermet coatings were also tested in the present
study; for example, microstructure, crystalline phases of as-sprayed coatings, and microhardness. Results present a
comparison of surface erosion wear of different cermet coatings. It was found that the yttrium oxide was a suitable
additive for the WOKA cermet coatings than the molybdenum carbide. However, zirconium oxide is unsuitable for
WOKA cermet coatings in erosion wear applications.

Keywords: Slurry erosion, HVOF coating, cermet, slurry pump, ash transportation