Improving Reaction to Fire Properties of Thermoplastic Polyurethane with Intumescent Flame Retardants and MoS2

Taghi-Akbari, Leila; Naimi-Jamal, Mohammad Reza; Ahmadi, Shervin

doi:10.22068/ijmse.3387

Volume 20, Issue 4 (December 2023) IJMSE 2023, 20(4): 1-8 | Back to browse issues page

‎ 10.22068/ijmse.3387

Mendeley

Zotero

RefWorks

Taghi-Akbari L, Naimi-Jamal M R, Ahmadi S. Improving Reaction to Fire Properties of Thermoplastic Polyurethane with Intumescent Flame Retardants and MoS2. IJMSE 2023; 20 (4) :1-8
URL: http://ijmse.iust.ac.ir/article-1-3387-en.html

Improving Reaction to Fire Properties of Thermoplastic Polyurethane with Intumescent Flame Retardants and MoS2

Leila Taghi-Akbari

, Mohammad Reza Naimi-Jamal

, Shervin Ahmadi

Abstract: (5220 Views)

Two-dimensional molybdenum disulfide (MoS₂) is used as a promising flame retardant and smoke suppressant nano additive in polymer composites due to its high thermal stability and layered structure. In this study, thermoplastic polyurethane (TPU) was melt-blended with MoS2 (1wt. %) and a halogen-free intumescent flame retardant (IFR) system. The IFR system consisted of ammonium polyphosphate (APP), Melamine polyphosphate (MPP), and pentaerythritol (PER), with a total amount of 25 wt. %. The TPU/IFR/MoS2 composite exhibited outstanding flame-retardant properties, achieving a UL-94 V-0 rating and a limiting oxygen index (LOI) value of 34%. Reaction-to-fire performance of the TPU/IFR/MoS2 composite was evaluated by cone calorimeter test (CCT). The CCT results indicated high flame-retardant efficiency and considerable smoke suppression performance, along with a significant decrease in the peak heat release rate (PHRR: 65.9%), peak smoke production rate (PSPR: 65.6%), and peak CO production (PCOP: 60.7%) compared to the neat TPU. The significant improvement in fire performance of TPU composite was mainly attributed to the effects of the physical barrier of MoS2 and catalytic carbonization of the IFR system. These resulted in forming an intumescent compact carbonized layer during the combustion, effectively restricting dripping. The continuous structure of the residual char was revealed by FESEM. Thermogravimetric analysis (TGA) indicated improved thermal behavior of the TPU composite in high temperatures. This work provides an effective method to improve the reaction to fire of TPU composites by incorporating traditional IFRs and MoS2, resulting in enhanced fire safety.

Keywords: Reaction to fire-, Intumescent flame retardant, MoS2, Thermoplastic polyurethane, Heat release rate