Showing 4 results for Mechanical Properties.
I. Ebrahimzadeh, Gh.h. Akbari,
Volume 6, Issue 1 (3-2009)
Abstract
Abstract: Horizontal continuous casting is widely used to produce semi-finished and finished metallic products.
Homogeneity in metallurgical characteristics and mechanical properties in such products is of importance. In the
present work microstructure and mechanical properties of a horizontal continuous cast pipe have been studied.
Microstructural features were investigated by an optical microscope equipped with image analyzer and SEM was used
to characterize precipitates. Tensile behavior, impact strength and hardness variations were the mechanical properties
which were studied. Results showed that microstructure and mechanical properties had diversities in different parts of
the pipe and distinct differences were observed between upper and lower parts of the pipe. A meaningful correlation
was found in microstructure and mechanical properties in different parts of the component.
A. Noorian, Sh. Kheirandish, H. Saghafian,
Volume 7, Issue 2 (6-2010)
Abstract
Abstract:
mechanical properties of AISIH 13 hot-work tool steel have been studied. Cast samples made of the modified new steel were homogenized and austenitized at different conditions, followed by tempering at the specified temperature ranges. Hardness, red hardness, three point bending test and Charpy impact test were carried out to evaluate the mechanical properties together with characterizing the microstructure of the modified steel using scanning electron microscope. The results show that niobium addition modifies the cast structure of Nb–alloyed steel, and increases its maximum hardness. It was found that bending strength bending strain, impact strength, and red hardness of the modified cast steel are also higher than those of the cast H13 steel, and lower than those of the wrought H13 steel.
In this research, the effects of partially replacing of vanadium and molybdenum with niobium on the
W. Orlowicz, M. Tupaj, M. Mróz, J. Betlej, F. Ploszaj,
Volume 9, Issue 1 (3-2012)
Abstract
Abstract: This study presents the research results of effect that refining process has on porosity and mechanical properties of high pressure die castings made of AlSi12S alloy. The operation of refining was carried out in a melting furnace with the use of an FDU Mini Degasser. Mechanical properties (UTS, YS, Elongation, Brinell Hardness) were assessed on samples taken from high pressure die castings. The effect of molten metal transfer operation and the time elapsing from completion of the refining process on the alloy mechanical properties was determined.
S. Kord, M. H. Siadati, M. Alipour, H. Amiri, P.g. Koppad, A. C. Gowda,
Volume 15, Issue 4 (12-2018)
Abstract
The effects of rare earth element, erbium (Er) additions on the microstructure and mechanical properties of Al-15Zn-2.5Mg-2.5Cu alloy have been investigated. This new high strength alloy with erbium additions (0.5, 1.0, 1.5 and 2.0 wt%) was synthesized by liquid metallurgy route followed by hot extrusion. Microstructural characterization was performed using scanning electron microscope and electron probe microanalysis. Significant amount of grain refinement was observed with erbium addition in the hot extruded and heat treated alloy. Tensile test was performed to investigate the effect rare earth on mechanical behavior of alloy in as cast and hot extruded condition before and after T6 heat treatment. The combined effect of erbium addition, hot extrusion and heat treatment significantly enhanced the tensile strength of alloy (602 MPa) when compared to the as cast alloy without erbium addition (225 MPa). The strengthening of the alloy was attributed to grain refinement caused by erbium along with hot extrusion and formation of precipitates after T6 heat treatment. Fractograhic investigations revealed that the hot extruded alloy with erbium addition after heat treatment showed uniformly distributed deep dimples exhibiting ductile behavior.