Showing 3 results for Relaxation
M. Ershadi Khameneh, H. Shahverdi, M. M. Hadavi,
Volume 12, Issue 4 (12-2015)
Abstract
Creep age forming (CAF) is one of the novel methods in aerospace industry that has been used to manufacture components of panels with improved mechanical properties and reduced fabrication cost. CAF is a combined age-hardening and stress-relaxation that are responsible for strengthening and forming, respectively. This paper deals with the experimental investigations of mechanical and springback properties of Al-Zn-Mg Al alloy in creep forming process. Creep forming experiments have been performed at temperatures of 120◦C and 180◦C for 6–72 h. Results indicated that yield stress and hardness of creep age formed specimens increased with increasing forming time and temperature, simultaneously induced deflection by stress-relaxation increased. Incorporating spring back and mechanical properties, it can be found that the appropriate forming cycle was 180 ◦C/24 h among all forming conditions. CAF Time increase to a certain extent increased mechanical properties. This can be attributed to presence of stress in CAF that causes the precipitates be finer because of creation more nucleation sites. Therefor the growth of precipitates, takes place at long time and postpones the decreasing of the yield stress
G. Chandraprabha, T. Sankarappa, T. Sujatha,
Volume 15, Issue 4 (12-2018)
Abstract
Polythiophene (PTh) and cobalt nanoparticles (Co-nps) were prepared by chemical oxidation and modified polyol processes respectively. Composites were made by mixing them in the proportions, PTh1-xCox; x = 0.1, 0.2, 0.3, 0.4, 0.5. Morphology of the samples has been studied by SEM technique. Dielectric properties with temperature and frequency as variables were investigated. Dielectric constant and loss factor decreased with frequency and increased with temperature. AC conductivity was estimated from the dielectric data. Ac conductivity decreased with increase of Co-nps in the composites which indicates that electrically insulating effect has been induced by Co-nps. Small polaron hopping mechanism is found to be the conduction mechanism operated. Activation energy for ac conduction decreased with increase of frequency and weight percent of Co-nps in the composites. Electric modulus was determined and its analysis leads to the estimation of dielectric relaxation time. Relaxation time decreased with increase of temperature for all the five composites. For the first time PTh-Co nanocomposites have been reported for dielectric properties and ac conductivity as a function of frequency and temperature.
Najwa Gouitaa, Lamcharfi Taj-Dine, Abdi Farid , Ahjyaje Fatima Zahra,
Volume 18, Issue 3 (9-2021)
Abstract
In this study we have synthesis the Zr substituted BaTi0.80Fe0.20O3 ceramics at different content of Zr from x=0.00 to 0.10 by using the solid-state route. The room temperature X-ray diffraction results confirmed the coexistence of the two tetragonal and hexagonal phases for x ≤ 0.050 of Zr content. While above 0.050 the hexagonal phase disappears in benefit of tetragonal phase. The Raman results confirmed the formation of these phases obtained with XRD. The scanning electron micrographs consist of both spherical and straight grain forms for x=0.000 to 0.075, and only spherical grain form for x=0.100 attributed to the tetragonal phase. Also, the grain size increases accompanied with a decrease in density of ceramics with increasing Zr content up to 0.050 then decreases accompanied with an increase in density. Detailed studies of dielectric permittivity measurement have provided a presence of two anomalies Te and TR-O at different temperatures, with a relaxation phenomenon and diffuse behavior which is very important for ceramic at x=0.075 of Zr content. The dielectric permittivity values of the two anomalies of Zr substituted BaTi0.80Fe0.20O3 ceramics increase with increase of Zr content and the dielectric loss is minimal at x=0.100 of Zr content. The conductivity increases with the increasing of Zr substitution from 0.025 to 0.075 levels while for x = 0.100 the dielectric conductivity decreases. And the Cole-Cole analysis indicates a negative thermal resistivity coefficient (NTCR) behavior of these materials and an ideal Debye-type behavior.